Diesters of halo-substituted alkylphosphonates

ABSTRACT

Novel compositions of matter comprising diesters of polyhalosubstituted alkylphosphonates as exemplified by dimethyl 3chloro-2,3-dibromopropylphosphonate are used as components in preparing compounds such as plastic, polymers, resins, etc. and will impart the desirable physical characteristics of flame retardancy or fire resistance to these compounds.

Elite States atent enghiat 1 Sept. 12, 1972 [54] DIESTERS OF HALO-SUBSTITUTED 3,193,570 7/1965 Fields ..260/96l X ALKYLPHOSPHONATES Primary Examiner-Joseph Rebold lsa hi N NY. [72] lnvfmor ac Bang ew Assistant Examiner-Anton H. Sutto AS51811! livers?! Oil Products Company Attorney-James R. Hoatson, Jr. and Raymond H.

Des Plames, Ill. Nelson [221 Filed: Dec. 29, 1969 57 ABSTRACT [21] Appl. No.: 888,965 1 Novel compositions of matter comprising diesters of polyhalo-substituted alkylphosphonates as exemplified [52] by dimethyl 3-chloro-2,3-dibromopropylphosphonate 260/999 are used as components in preparing compounds such 511 Int. Cl. "cam 9/40, C08f 45/58 as Plastic, P Y resins and will impart the 58 Field of Search ..260/96l desirable physical characteristics of flame retardancy or fire resistance to these compounds.

[56] 5 Claims, No Drawings UNITED STATES PATENTS DIESTERS OF HALO-SUBSTITUTED ALKYLPHOSPHONATES This invention relates to novel compositions of matter comprising diesters of polyhalo-substituted alkylphosphonates. More specifically, the invention is concerned with dialkyl esters of polyhalo-substituted alkylphosphonates in which said polyhalo substituents constitute at least two dissimilar halogen atoms and the use thereof as a component of finished compositions of matter which possess a high degree of flame retardan- It has now been discovered that the flame retardancy or fire resistance of many compounds such as polymers, resins, etc., may be enhanced by the addition of a diester of a polyhalo-substituted alkylphosphonate, the degree of flame retardancy being further enhanced if the polyhalo substituents in the compound constitute at least two dissimilar halogen atoms. Some examples of compounds which may be admixed with the phosphonate of the type hereinafter set forth in greater detail will include plastics, polymers, resins as well as naturally occurring textiles and fibers, specific examples of these compounds including polyolefins such as polyethylene, polypropylene, polystyrene and copolymers thereof, polyesters, polyurethanes, polyphenyl ethers such as polyphenylene oxides, polycarbonates, polyamides, polyoxymethylenes, polyalkylene oxides such as polyethylene oxide, polyacetals, polyacrylates, polymethacrylates, epoxy resins, copolymers or graft polymers of acrylonitrile with styrenic olefins such as acrylonitrile-butadienestyrene formulations (commonly known as ABS), both naturally occurring and synthetic rubber such as polyisoprene, polybutadiene, EPR rubber, SBR rubber, textiles, fibers, fabrics, said textiles, fibers and fabrics being both naturally occurring and synthetic in nature, coatings, paints, varnishes, leathers, foam, etc. By combining these aforementioned compounds with a diester of a polyhalo-substituted alkylphosphonate of the type hereinafter set forth in greater detail, the compounds will possess the desirable physical characteristics of flameproofing or fire retardancy. These particular physical characteristics will possess special advantages when preparing plastics, polymers, resins, various rubbers, textiles, etc. which will be utilized in places which may be subjected to excessive heat or to the action of a possible flame, such places including architectural panels for construction work, wall plugs for electrical connections, soundproofing material in walls, ceilings, etc., cushions for various vehicle seats such as airplane seats, automobile seats, bus seats, etc. In addition, the compound when utilized as a constituent of paint, lacquer, varnishes, or protective coatings, films, etc., will also impart a flame resistancy to these compounds and, therefore, render them commercially attractive as articles of commerce. In addition, it is also contemplated that the novel compositions of matter comprising a diester, and particularly a dialkyl ester, of a polyhalo-substituted alkylphosphonate in which the halo substituents positioned on the alkyl portion of the phosphonate will comprise two dissimilar halogen atoms, may also be useful as insecticides, and particularly against houseflies.

It is therefore an object of this invention to provide novel compositions of matter which possess desirable physical characteristics or properties.

Another object of this invention is to provide novel compositions of matter possessing these desirable physical characteristics of flameproofing and fire retardancy whereby said compositions of matter may be useful as components of finished important commercial articles of manufacture.

In one aspect an embodiment of this invention resides in a novel composition of matter comprising a diester of a polyhalo-substituted alkylphosphonate in which said polyhalo substituents constitute at least two dissimilar halogen atoms.

Another embodiment of this invention resides in a flame retardant composition of matter comprising a polymer and an effective concentration of a diester of a polyhalo-substituted alkylphosphonate in which said polyhalo substituents constitute at least two dissimilar halogen atoms.

A specific embodiment of this invention is found in a novel compound comprising dimethyl 3-chloro-2,3- dibromopropylphosphonate.

Another specific embodiment of this invention is found in a flame retardant composition of matter comprising an admixture of a polyester and dimethyl 3- chloro-2,3-dibromopropylphosphonate.

Other objects and embodiments will be found in the following further detailed description of the present invention.

As hereinbefore set forth the present invention is concerned with novel compositions of matter which comprise diesters of polyhalo-substituted alkylphosphonates, and particularly dialkyl esters of polyhalo-substituted alkylphosphonates in which the halogen substituents comprise at least two dissimilar halogen atoms. The aforementioned novel compositions of matter will possess the generic formula R eii'iiaom l i. i

in which X is hydrogen or halogen atoms, preferably chlorine or bromine, at least two Xs being halogen, R is an alkyl radical of from one to about five carbon atoms, R and R" are independently selected from the group consisting of hydrogen, halogen, lower alkyl of from one to five carbon atoms, cycloalkyl, aryl, aralkyl, alkaryl and halogenated derivatives thereof, at least two of the halogen atoms in the compound being dissimilar in nature.

Some representative specific examples of the novel compositions of matter of the present invention which possess the generic formula hereinbefore set forth will include dimethyl 3-chloro-2 ,3- dibromopropylphosphonate, dimethyl 4-chloro-2,3- dibromobutylphosphonate, dimethyl 5-chloro-2,3- dibromopentylphosphonate, dimethyl 4-chloro-4- cyclohexyl-2,3-dibromobutylphosphonate, dimethyl 4- chloro-4-phenyl-2,3-dibromobutylphosphonate,

dimethyl 3-chloro-3-( p-tolyl )-2 ,3- ,dibromopropylphosphonate, dimethyl 3-chloro-3- benzyl-2,3-dibromopropylphosphonate, diethyl 3- chloro-2,3-dibrompropylphosphonate, diethyl 4- chloro-2,3-dibromobutylphosphonate, diethyl 5- chloro-2,3-dibromopentylphosphonate, diethyl 4- chloro-4-cyclohexyl-2,3-dibromobutylphosphonate, diethyl 4-chloro-4-phenyl-2,3-dibromobutylphosphonate, diethyl 3-chloro-3-(p-tolyl)-2,3- dibromopropylphosphonate, diethyl 3-chloro-3-benzyl- 2,3-dibromopropylphosphonate, dipropyl 3-chloro- 2,3-dibrompropylphosphonate, dipropyl 4-chloro-2,3- dibromobutylphosphonate, dipropyl 5-chloro-2,3- dibromopentylphosphonate, dipropyl 4-chloro-4- cyclohexyl-Z,3-clibromobutylphosphonate, dipropyl 4- chloro-4-phenyl-2,3-dibromobutylphosphonate,

dipropyl 3-chloro-3 p-tolyl )-2,3- dibromopropylphosphonate, dipropyl 3-chloro-3- benzyl-2,3-dibromopropylphosphonate, dibutyl 3- chloro-2,3-dibromopropylphosphonate, dibutyl 4- chloro-2,3-dibromobutylphosphonate, dibutyl 5- chloro-2,3-dibromopentylphosphonate, dibutyl 4- chloro-4-cyclohexyl-2 ,3-dibrom obutylphosphonate dibutyl 4-chloro-4-phenyl-2,B-dibromobutylphosphonate, dibutyl 3-chloro-3-(p-tolyl)-2,3- dibromopropylphosphonate, dibutyl 3-chloro-3- benzyl-2,3-dibromopropylphosphonate, dipentyl 3- chloro-2,3-dibromopropylphosphonate, dipentyl 4- chloro-2,3-dibromobutylphosphonate, dipentyl 5- chloro-2,3-dibromopentylphosphonate, dipentyl 4- chloro-4-cyclohexyl-2,3-dibromobutylphosphonate, dipentyl 4-chloro-4-phenyl-2,3-dibromobutylphosphonate, dipentyl 3-chloro-3-(p-tolyl)-2,3- dibromopropylphosphonate, dipentyl 3-chloro-3- benzyl-2,3-dibrom0propylphosphonate, etc. It is to be understood that the aforementioned compounds are only representative of the class of novel compositions of matter, and that the present invention is not necessarily limited thereto.

The novel compositions of matter of the type hereinbefore set forth may be prepared by reacting a dichloro-substituted alkene with a trialkyl phosphite in the presence of an organic solvent at condensation conditions. These condensation conditions will include a temperature in the range of from about 100 to about 200C., and preferably at the reflux temperature of the particular solvent if one is employed in the reaction. Generally speaking, the reaction may also be effected at pressures ranging from atmospheric up to about 50 atmospheres or more, the preferred pressure being atmospheric. Some specific examples of starting materials which may be condensed will include 1,3- dichloropropene, 2,3-dichloropropene-l 1,4- dichlorobutene-2, 1,4,4-trichlorobutene-2, 1,5- dichloropentene-Z, 1,6-dichlorohexene-2, 1,5,5- trichloropentene-Z, 1,6,6-trichlorohexene-2, 1,2,3- trichloropropene, l,2,4-trichlorobutene-2, 1,2,5-

trichloropentene-Z, 4-cyclohexyl-1,4-dichlorobutene- 2, 4phenyl 1,4-dichlorobutene-2, 3-(p-tolyl)-l,3- dichloropropene-2, 3-benzyl-l ,3-dichloropropene-2, 4- benzyl-l ,4-dichlorobutene-2, 4-(p-tolyl)-l ,4- dichlorobutene-Z, 3-cyclohexyl-l,3-dichloropropene- 2, etc.

The aforementioned polyhalo-substituted polyalkenes are condensed with alkyl phosphites in which the alkyl substituent may contain from one to about five carbon atoms. Specific examples of these compounds will include trimethyl phosphite, triethyl phosphite, tripropyl phosphite, triisopropyl phosphite, tributyl phosphite, tri-t-butyl phosphite, triamyl phosphite, trisec-amyl phosphite, etc. lt is to be understood that the aforementioned specific examples of the polyhalo-substituted alkenes and alkyl phosphites are only representative of the class of compounds which may be used,

and that the present invention is not necessarily limited thereto.

The condensation of the two reactants is effected at condensation conditions within the range hereinbefore set forth in the presence of a substantially inert organic solvent. Some specific examples of these organic solvents will include dimethylformamide, diethylformamide, dipropylformamide, dimethylacetamide, diethylacetamide, dipropylacetamide, etc. It is also contemplated that other solvents such as alcohols include methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, etc.; aromatic solvents such as benzene, toluene, xylenes, ethylbenzene, etc.; paraftinic solvents such as n-heptane, n-hexane, cyclopentane, methylcyclopentane, cyclohexane, etc., or simple ethers such as dimethyl ether, diethyl ether, dipropyl ether may also be used at elevated pressures if necessary, although not necessarily with equivalent results.

The compound which results from the condensation of the dichloro-substituted alkenes and alkyl phosphite which comprises a chloro-substituted alkenylphosphonate is then subjected to a bromination step by treating said phosphonate with a brominating agent comprising hydrogen bromide or elemental bromine in the presence of an organic solvent at bromination conditions. These bromination conditions will include temperatures ranging from about 0 C. up to about C., the preferred temperature being at the reflux temperature in the particular solvent which is employed in the reaction and at atmospheric pressure. Upon completion of the addition of the brominating agent the solvent which is employed is removed by conventional means and the desired product is recovered. Examples of solvents which may be employed in the bromination process will include halo-substituted alkanes such as chloroform and carbon tetrachloride or aromatic solvents such as benzene, chlorobenzene, etc.

The process for preparing the aforementioned novel compositions of matter may be effected in any suitable manner and may comprise either a batch or continuous type operation. As one example of a method of preparation, when a batch type operation is used, a quantity of the starting materials comprising the polychloro-substituted alkene and the trialkyl phosphite are placed in an appropriate apparatus such as a flask provided with heating, stirring and reflux means. In addition, the flask will also contain the particular solvent which is to be employed. Generally speaking, the reactants are present in the reaction mixture in a molar ratio. The reactor is then heated to the desired operating temperature which, as hereinbefore set forth, preferably constitutes the reflux temperature of the particular solvent which is employed in the reaction. The condensation is allowed to proceed at reflux temperature for a predetermined period of time which may range from about 0.5 up to-about 10 hours or more in duration, the end of the reaction being attained when there is a cessation of the evolution of alkyl chloride. The reaction mixture is recovered and subjected to fractional distillation whereby the desired product is separated from solvent, unreacted starting materials and/or unwanted side reactions which may have occurred during the condensation period.

The chloro-substituted alkenylphosphonate which constitutes the desired reaction product of the above condensation is then placed in a second reaction vessel also provided with heating or cooling, stirring and reflux means. In addition, the desired solvent of the type hereinbefore set forth is also present in this reactor. Following this the brominating agent is slowly added to the reactor for a predetermined period of time and the reactor is heated to the reflux temperature of the particular solvent. It is contemplated within the scope of this invention that the brominating agent, if in elemental form, may be added as a solution in the same solvent which is present in the reaction vessel. After the addition of the brominating agent has been completed, usually in an equimolar amount to the chloro+substituted alkenylphosphonate which is present in the reactor, the reaction mixture is refluxed for an additional period, the total contact time ranging from 1 to about hours or more in duration, the completion of the reaction being attested to by the disappearance of the bromine color. Upon completion of the bromination reaction heating is discontinued and the reaction mixture is recovered from the apparatus. This reaction mixture is also subjected to distillation whereby the solvent is separated and the desired product comprising the diester of the polyhalo-substituted phosphonate containing both chlorine and bromine atoms 'is recovered.

It is also contemplated within the scope of this invention that the preparation of the desired novel compositions of matter may be accomplished by utilizing a continuous manner of operation, although not necessarily with equivalent results. When such a type of operation is used the starting materials comprising the polychloro-substituted alkene and the trialkyl phosphite are continuously charged to a reaction vessel which is maintained at the proper operating conditions of temperature and pressure. If so desired, the solvent in which the reaction is effected may be admixed with one or both of the starting materials prior to entry into said reactor or, in the alternative, said solvent may be charged to the reactor through a separate line. Upon completion of the desired residence time the reactor effluent is continuously withdrawn and subjected to separation means such as fractional distillation whereby the desired product comprising the chlorosubstituted alkenylphosphonate is separated from solvent and unreacted starting materials, the latter two being recycled to form a portion of the feed stock, while the former is charged to a second reaction vessel also maintained at the proper operating conditions of temperature and pressure. In this second reactor the brominating agent, either hydrogen bromide or elemental bromine is also continuously charged at a predetermined rate. In addition, the solvent in which the reaction is effected may be charged to the reactor through a separate line or admixed with the chloro-substituted alkenylphosphonate prior to entry into said reactor and the resulting solution charged thereto through a single line. Upon completion of the desired residence time the reactor effluent from the second reactor is continuously discharged and again subjected to conventional separation means such as, for example,

fractional distillation whereby the desired diester of the polyhalo-substituted alkylphosphonate containing both chlorine and bromine atoms is recovered while the solvent is recycled back to the second reactor.

While the general method for the synthesis described herein is satisfactory for the preparation of the compounds which comprise the novel compositions of matter of the present invention, I do not wish to be limited to these preparational procedures, and therefore any other appropriate methods which are known to those skilled in the art may also be utilized to prepare these compounds.

The aforementioned novel compositions of matter of the present invention are utilized, as hereinbefore set forth, as components in the preparation of finished compounds which will possess flame retardant or fire resistant properties, said diesters of polyhalo-substituted alkylphosphonates comprising from about 5 to about 50 percent of the finished product, the other component of the finished product comprising a polymer. The desired finished products may be prepared in any suitable manner such as, for example, by admixing the compounds in a mixer, by milling the components, or by extruding the components through a suitable apparatus after admixture thereof, the only criterion being that the two components of the mixture are thoroughly admixed in such a fashion so that the components are uniformly distributed throughout the finished product.

Some representative examples of the compounds comprising the finished product of the present invention will include polypropylene and dimethyl 3-chloro- 2,3-dibromopropylphosphonate, ABS and dimethyl 3- chloro-2,3-dibromopropylphosphonate, polyethylene oxide and dimethyl 3-chloro-2,3- dibromopropylphosphonate, polyester and dimethyl 3- chloro-2,3-dibromopropylphosphonate, polyethylene and dimethyl 3-chloro-2,3- dibromopropylphosphonate, polyurethane and dimethyl 3-chloro-2,3-dibromopropylphosphonate, polyphenylene oxide and dimethyl 3-chloro-2,3- dibromopropylphosphonate, polypropylene and diethyl 3-chloro-2,3-dibromopropylphosphonate, ABS and diethyl 3-chloro-2,3-dibromopropylphosphonate, polyethylene oxide and diethyl 3-chloro-2,3- dibromopropylphosphonate, polyester and diethyl 3- chloro-2,3-dibromopropylphosphonate, polyethylene and diethyl 3-chloro-2,3-dibromopropylphosphonate, polyurethane and diethyl 3-chloro-2,3 dibromopropylphosphonate, polyphenylene oxide and diethyl 3-chloro-2,3-dibromopropylphosphonate, polypropylene and dimethyl 3-chloro-2,3-dibromobutoxymethylphosphonate, ABS and dimethyl 3-chloro- 2,3-dibromobutoxymethylphosphonate, polyethylene oxide and dimethyl 3-chloro-2,3-dibromobutoxymethylphosphonate, polyester and dimethyl 3-chloro- 2,3-dibromobutoxymethylphosphonate, polyethylene and dimethyl 3-chloro-2,3-dibromobutoxymethylphosphonate, polyurethane and dimethyl 3- chloro-2,3-dibromobutoxymethylphosphonate, polyphenylene oxide and dimethyl -3-chloro-2,3- dibromobutoxymethylphosphonate, polypropylene and dipropyl 3-chloro-3-benzyl-2,3- dibromopropylphosphonate, ABS and dipropyl 3- chloro-3-benzyl-2,3-dibromopropylphosphonate, polyethylene oxide and dipropyl 3-chloro-3-benzyl-2,3- dibromopropylphosphonate, polyester and dipropyl 3- chloro-3-benzyl-2,3-dibromopropylphosphonate, polyethylene and dipropyl 3-chloro-3-benzyl-2,3- dibromopropylphosphonate, polyurethane and dipropyl 3-chloro-3-benzyl-2,3- dibromopropylphosphonate, polyphenylene oxide and dipropyl 3-chloro-3-benzyl-2,3- dibromopropylphosphonate, etc. it is to be understood that the aforementioned compounds which possess flame retardant properties are only representative of the class of compounds which may be prepared, and that the present invention is not necessarily limited thereto.

it is also contemplated within the scope of this invention that the finished product of the type hereinbefore set forth, that is, a polymer and dialkyl ester of a polyhalo-substituted alkylphosphonate may also contain a sufficient amount of a tin and/or antimony compound which will act as a synergist for the flame retardant property of said finished compound by enhancing the desirable characteristic. Some specific examples of the tin and antimony compounds which may be used will include tin compounds in a tetravalent state such as tin dioxide, tin tetrachloride, methyl tin trichloride, ethyl tin trichloride, butyl tin trichloride, dipropyl tin dichloride, trimethyl tin chloride, methyl tin triacetate, dipropyl tin diacetate, diethyl tin dipropionate, diethyl tin dimaleate, dibutyl tin dimaleate, methyl tin trimaleate, dibenzyl tin dichloride, dimethyl tin sulfide, diethyl tin sulfide, dimethyl tin bis(methylmercapti'de), dibutyl tin bis( octylmercaptide), diethoxy tin bis(ethylmercaptide), tin tetrakis(methylmercaptide), tin tetrakis(phenylmercaptide), diethyl tin mercaptoacetate, dioctyl tin mercaptoacetate, dihexyl tin mercaptopropionate, dimethyl tin mercaptobutyrate, dioctyl tin mercaptobutyrate, dilauryltin dithiobutyric acid ethyl ester, diethyl tin S,S' bis-(3,5,5,-trimethylhexyl mercaptoacetate), dibutyl tin S,S bis(phenoxyethyl mercaptoacetate), dibutyl tin S,S' bis(diethylene glycol laurate mercaptoacetate), etc., antimony trioxide, antimony oxychloride, etc. It is to be understood that these compounds are only representative of the synergistic additives which may be admixed with the polymer and the phosphonate, and that the present invention is not necessarily limited thereto.

As will be hereinafter shown in the specific examples, the novel compositions of matter comprising the diesters of halo-substituted alkylphosphonates containing dissimilar halogen atoms as substituents thereof will impart an unexpectedly high degree of fire retardancy when utilized as components in finished products as compared to compounds which do not possess all of the components hereinafter claimed.

The following examples are given to illustrate the process of the present invention which, however, are not intended to limit the generally broad scope of the present invention in strict accordance therewith.

EXAMPLE I In this example a novel composition of matter of the present invention was prepared by placing 66.6 G. (0.6 mole) of 1,3-dichloropropene, 74.4 g. (0.6 mole) of trimethyl phosphite and 7.7 g. of dimethylformamide in a flask provided with heating stirring and refluxing means. The mixture was heated to reflux and maintained thereat for a period of 6.5 hours, the temperature of the mixture rising from 122 to 165C. during this period. When the evolution of methyl chloride ceased, heating was discontinued and the mixture allowed to return to room temperature. The reaction mixture was recovered and subjected to fractional distillation, the fraction boiling at 114 118C. at 8 mm. pressure comprising dimethyl 3-chloroallylphosphonate being recovered.

A solution of cc. of carbon tetrachloride and 36.9 g. (0.2 mole) of the dimethyl 3-chloroallylphosphonate which was prepared according to the processes of the above paragraph was placed in a flask similar to that used in paragraph one above and heated to reflux (about 77C.). To this refluxing solution was added a solution of 32 g. (0.2 mole) of elemental bromine in 40 cc. of carbon tetrachloride, said bromine being added dropwise during a period of about 90 minutes. Upon completion of the addition of the bromine the reaction mixture was refluxed for a period of about 5 hours until the bromine color had disappeared. The solution was then subjected to fractional distillation under reduced pressure whereby the carbon tetrachloride solvent was removed. The remaining product comprised dimethyl 3-chloro-2,3-dibromopropylphosphonate. An elemental analysis was effected with the following results. Calculated For C H Br ClO P: Cl, 10.3 percent Found: Cl, 10.5 percent EXAMPLE II In this example an equimolar mixture of 66.6 g. (0.6

mole) of 1,3-dichloropropene and 99.6 g. (0.6 mole) of triethyl phosphite along with 8 g. of dimethylformamide are placed in a flask similar to that used in the above experiment. The flask is heated to reflux temperature and maintained thereat for a period of about 7 hours until the evolution of ethyl chloride ceases. The mixture is then subjected to fractional distillation under reduced pressure and the desired product comprising diethyl 3-chloroallylphosphonate is separated out and recovered.

A solution of42.5 g. (0.2 mole) of diethyl 3-chloroallylphosphonate which is prepared according to the above paragraph in 60 cc. of carbon tetrachloride is heated to reflux in an apparatus comprising a flask provided with heating, stirring and reflux means. Thereafter a solution of 32 g. (0.2 mole) of elemental bromine in 40 cc. of carbon tetrachloride is slowly added dropwise to this refluxing solution. Upon completion of the addition the resulting mixture is refluxed for a period of about 5 hours until the bromine color has disappeared. Upon completion of the desired residence time the mixture is subjected to fractional distillation under reduced pressure in order to remove the carbon tetrachloride solvent, the desired product comprising diethyl 3-chloro- 2,3dibromopropylphosphonate being recovered therefrom.

EXAMPLE III An equimolar mixture of g. (0.6 mole) of 1,4- dichlorobutene-Z and 74.4 g. (0.6 mole) of trimethyl phosphite along with 10 g. of diethylformamide is heated at reflux until the evolution of methyl chloride is practically ceased, the temperature rising during the reflux period which extends over a period of 6.5 hours. At the end of this time the solution is subjected to fractional distillation under reduced pressure and the desired dimethyl 4-chlorobutenylphosphonate is recovered therefrom.

To a solution maintained at reflux temperature comprising 39.7 g. (0.2 mole) of dimethyl 4-chlorobutenylphosphonate in 60 cc. of carbon tetrachloride is slowly added a solution of 32 g. (0.2 mole) of elemental bromine in 40 cc. of carbon tetrachloride, said addition being effected dropwise during a period of about 90 minutes. Upon completion of the addition the solution is refluxed for an additional period of hours until the bromine color has disappeared. The solution is then subjected to fractional distillation under reduced pressure to remove the carbon tetrachloride, the remainder being the desired product comprising dimethyl 4- chloro-2,3-dibromobutylphosphonate.

EXAMPLE IV The reaction set forth in example III above is repeated, the difference being the use of 99.6 g. (0.6 mole) of triethyl phosphite in place of the 74.4 g. of trimethyl phosphite which is reacted with 1,4- dichlorobutene-2. The desired product which is recovered by fractional distillation comprises diethyl 4- chlorobutenylphosphonate. This product is then treated with elemental bromine in a manner similar to that hereinbefore set forth whereby, after fractional distillation under reduced pressure to remove the carbon tetrachloride solvent, the desired product comprising diethyl 4-chloro-2,3-dibromobutylphosphonate is recovered.

EXAMPLE V A polyester was prepared in a conventional manner by admixing 1 mole of maleic anhydride, 1 mole of maleic anhydride, 1 mole of phthalic anhydride and 2 moles of propylene glycol to a final temperature of 195C. The resultant ester was mixed with styrene following which the ester was divided into two portions. To one portion of the polyester was added a sufficient amount of the compound prepared according to example I above, that is, dimethyl 3-chloro-2,3- dibromopropylphosphonate so that the finished compound contained l5 parts per hundred of the phosphonate per hundred parts of resin. The untreated polyester was labeled A while the treated polyester was labeled B. The two esters were then treated with a catalyst and poured into molds. Following this, the casts were cured in an air oven. The casts were burned in an apparatus similar to that described by C. P. Fennimore and J. F. Martin in the November, 1966 issue of Modern Plastics. The cast which contained only the polyester (A) had an oxygen index (the lowest mole fraction of oxygen sufficient to maintain combustion) of n 0.187. In contrast to this, the oxygen index of the polyester cast which contained the dimethyl 3-chloro- 2,3-dibromopropylphosphonate (B) had an oxygen index of 0.239. Inasmuch as the oxygen index of air is 0.21, it should be noted that the polyester containing the phosphonate would not support combustion in an ordinary environment and that a higher concentration of oxygen would have to be present in order that combustion of this composition of matter would occur.

dibromopropylphosphonate which is prepared according to the process set forth in example I above so that the finished product will contain 15 percent by weight of the phosphonate. Thereafter the resulting compound is formed into a strip which will contain a glass cloth in the center thereof to prevent dripping during the combustion test. A second strip consisting of only polypropylene is also prepared and thereafter both strips are subjected to a flammability test similar to that set forth in example I above. The oxygen index of the strip which contains only polypropylene will be 0.181 while the strip which comprises polypropylene and the phosphonate compound will exhibit a burning rate which is far slower than the strip which contains no flame retardant and, in addition, will possess a greater than average oxygen index.

EXAMPLE VI] A commercial polyethylene oxide is milled and cut into a strip similar in nature to the polypropylene strip which was prepared in example VI above. Another sample is prepared by admixing polyethylene oxide and dimethyl 4-chloro-3,4-dibromobutylphosphonate in sufficient amounts so that the finished polymer will contain 15 percent of the phosphonate compound. The untreated and treated strips of polyethylene oxide are also subjected to a flammability test utilizing an apparatus similar to that set forth in example V above. The oxygen index of the untreated polyethylene oxide is 0.150 while the oxygen index of the compound of the present invention will be substantially in excess of this number and, in addition, will have a much slower burning rate than that of the untreated polyethylene oxide.

EXAMPLE VIII In this example a commercial acrylonitrile-bu tadiene-styrene formulation is admixed with dimethyl 3-chloro-2,3-dibromopropylphosphonate, the finished product containing 15 percent ,by weight of the phosphonate compound. This mixture is extruded as rods having a diameter of 0.5 cm. In addition, another rod of similar diameter is prepared which contains only the commercial ABS formulation. Following this the rods are burned in a flammability test utilizing an apparatus which is similar in nature to that referred to in example V above. The rod which contains only the commercial ABS formulation will have an oxygen index of 0.183 while, in contrast to this, the oxygen index of the ABS formulation containing the phosphonate will be greatly in excess of this number.

EXAMPLE IX A novel compound of the present invention is prepared by milling a commercial polyethylene formulation with diethyl 3-chloro-2,3- dibromopropylphosphonate in sufficient quantities so that the finished formulation will contain about 16 percent by weight of the finished compound. The thus formed polymer is cut into strips which contain a glass cloth in the center of the strip to prevent dripping during combustion. In addition, commercial polyethylene, per se, is milled and also cut into strips of similar configuration. The two strips are then subjected to a flammability test similar in nature to that described in example V above. The results of these tests will show in which X is hydrogen or halogen atoms, at least two Xs being halogen, R is an alkyl radical of from one to about five carbon atoms, R and R" are independently selected from the group consisting of hydrogen, halogen, lower alkyl of from one to five carbon atoms and cycloalkyl, aryl, aralkyl, and alkaryl compounds containing up to seven carbon atoms and halogenated derivatives thereof, at least two of the halogen atoms in the compound being dissimilar in nature.

2. The novel composition of matter of claim 1 being dimethyl 3-chloro-2,3-dibromopropylphosphonate.

3. The novel composition of matter of claim 1 being diethyl 3-chloro-2,3-dibromopropylphosphonate.

4. The novel composition of matter of claim 1 being dimethyl 4-chloro-2,3-dibromobutylphosphonate.

5. The novel composition of matter of claim 1 being diethyl 4-chloro-2,3-dibromobutylphosphonate. 

2. The novel composition of matter of claim 1 being dimethyl 3-chloro-2,3-dibromopropylphosphonate.
 3. The novel composition of matter of claim 1 being diethyl 3-chloro-2,3-dibromopropylphosphonate.
 4. The novel composition of matter of claim 1 being dimethyl 4-chloro-2,3-dibromobutylphosphonate.
 5. The novel composItion of matter of claim 1 being diethyl 4-chloro-2,3-dibromobutylphosphonate. 